合金鋁板壓型加工時是鋁卷在壓型設備（彩鋼瓦設備）上面加工，類似于滾邊、折邊加工工藝，將鋁板加工為各種型號的壓型鋁板，主要用于屋面、電廠脫硫、防腐保溫等行業中。

During the compression processing of alloy aluminum sheets, aluminum coils are processed on the compression equipment (color steel tile equipment), similar to the rolling and folding processing technology. The aluminum sheets are processed into various types of compression aluminum sheets, mainly used in industries such as roofs, power plant desulfurization, anti-corrosion and insulation.

鋁板壓型加工的常見規格：通常鋁板都是壓型YX35-125-750型號為常用，尤其是電廠防腐保溫工程、煙道脫硫防腐工程為常用，厚度以0.5-1.2mm厚度居多，材質常常為1060、3003、3A21、LF21等材質。

Common specifications for aluminum plate pressing processing: Usually, YX35-125-750 aluminum plates are commonly used, especially in power plant anti-corrosion and insulation engineering, flue desulfurization and anti-corrosion engineering. The thickness is mostly 0.5-1.2mm, and the materials are often 1060, 3003, 3A21, LF21, and other materials.

第二種常見的鋁板壓型加工型號為YX23-210-840型號，常常擁有屋面和墻面方面，我們稱為840型壓型鋁板，有時候許多工廠和車間的屋面采用彩涂鋁卷進行壓型常常選擇840型號的壓型鋁板。

The second common aluminum plate pressing processing model is YX23-210-840 model, which often has roof and wall aspects. We call it 840 type pressed aluminum plate. Sometimes, many factories and workshops use colored coated aluminum coils for pressing on the roof, and often choose 840 type pressed aluminum plate.

鋁板在壓型加工過程中要注意壓型鋁板的長度和厚度，避免因為設備問題導致的壓型鋁板邊緣部位因為磨損導致的毛刺。在鋁板的壓型加工以后包裝的適合也要注意防水防潮。同時在選擇鋁板材質方面建議不要選擇硬度太高的產品，通?？蛇x擇H24或者H16狀態的鋁卷作為鋁板壓型加工的原料，如果鋁板硬度太高會導致加工過程中斷裂問題。

During the pressing process of aluminum plates, attention should be paid to the length and thickness of the pressed aluminum plates to avoid burrs at the edges of the pressed aluminum plates caused by wear and tear due to equipment issues. After the compression processing of the aluminum plate, the packaging should also pay attention to waterproofing and moisture prevention. At the same time, it is recommended not to choose products with high hardness when selecting aluminum plate materials. Generally, aluminum coils in H24 or H16 state can be selected as the raw material for aluminum plate pressing processing. If the aluminum plate hardness is too high, it will cause fracture problems during the processing.

壓型加工中常見問題：壓型加工中的問題主要是鋁卷平整度不行，容易跑偏，所以想要壓型過程中不跑偏建議采用拉彎矯處理，校平平整度，就能夠很好的避免鋁板壓型過程中的跑偏。山東泰格鋁業有限公司常年提供各種優質的壓型鋁板，適合于電力、屋面、設備罐體等各種設備使用，現貨供應厚度0.5毫米、0.6毫米、0.7毫米、0.8毫米、1毫米等各種厚度的壓型鋁板和

Common problems in compression molding: The main problem in compression molding is the poor flatness of the aluminum coil, which is prone to deviation. Therefore, if you want to avoid deviation during the compression process, it is recommended to use tension bending correction to level the flatness, which can effectively avoid deviation during the aluminum plate compression process. Shandong Taige Aluminum Industry Co., Ltd. provides various high-quality profiled aluminum sheets year-round, suitable for use in various equipment such as power, roofs, and equipment tanks. In stock, we supply profiled aluminum sheets with thicknesses of 0.5mm, 0.6mm, 0.7mm, 0.8mm, 1mm, and other thicknesses